    1. Patent Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating
    2. Patent Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating
    3. Patent Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating
    4. Patent Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating
    5. Patent Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating

    Patent Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating

    • Type:NanoX, NanoY
    • Brand :AdvancedMetal
    • Sizes:8-25um, 15-45um, 2-10um, 25-90um etc.

    NanoX is Nickel Self-fluxing Alloy improved from Hastelloy, of Amorphous + Nanocrystalline microstructure. Fine powder for Tube Inside ID coating and very smooth finish. Coating is higher Amorphous rate than Powder. Coating thickness over 50um is airtight and very economic replacing chrome plating. The coating properties 1. better corrosion resist than Hastelloy or Inconel and Stellite, resist pure Acid or Alkali. 2. hardness HV700-900 and Abrasion resist. 3. temperature resist up to 1000℃. 4. good bonding strength. 5. for HVAF or HVOF, Plasma or Detonation Spraying, Bond Coat.

    1. Detailed information

    Amorphous Nickel Spraying Powder NanoX Better Corrosion than Hastelloy, 

    HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating

    AMTmetalTech Nickel Amorphous HVOF or HVAF Thermal Spraying Cylinders Powder   AMTmetalTech Tube Inside ID HVOF or HVAF Spraying Hastelloy or Stellite Powder   AMTmetalTech Tube Inside ID HVOF or HVAF Powder Therml Spraying Inconel Powder  AMTmetalTech Nickel Amorphous Spraying Powder Replacing Chrome Plating

    1. Amorphous Nickel Spraying Powder of Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating Description

    AMTmetalTech patent Gas Atomized Powder NanoX and NanoY are Nickel Self-fluxing Alloy improved from Hastelloy. Both are of uniform Amorphous+Nanocrystalline microstructure, with sizes 8-25, 15-45, 2-10, 25-90um etc. Fine powder can be for Tube Inside ID coating and the finish is very smooth. After metal thermal spraying in some lower heat input than Tungsten Carbide powder and with rapid cooling, the Coating can achieve higher Amorphous rate than in the powder. The NanoX coating can have porosity lower than 0.1%, deposition rate about 50% and the coating of thickness over 50um can be no need sealing and very economic for replace chrome plating. The NanoY coating can have porosity about 1% and the deposition rate about 70%.

    NanoX and NanoY Powder Sizes Choice: 

    1.1 Size 8-25um is for various Guns of Axial or Center Direction powder feeding. 

    1.2 Size 15-45um is for various Guns of Radial or Vertical Direction powder feeding. 

    1.3 Size 2-10um is for Guns of Inside Diameter ID under 80mm tube inside coating. 

    1.4 Size 25-90um is for Plasma or Detonation Spraying.

    2.Amorphous Nickel Spraying Powder of Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating Properties

    2.1 better corrosion resist than Hastelloy C276 or Inconel625 and Stellite6 or 12, can resist pure Acid or pure Alkali. 

    2.2 high hardness HV700-900 and have very good Abrasion resist. 

    2.3 can resist high temperature up to 1000℃. 

    2.4 good bonding strength. 

    2.5 can be used for HVAF or HVOF thermal spraying, Plasma or Detonation Spraying, act as Bond Coat or Tube Inside ID coating.

    Type

    Chemical Composition(%)

    Nano Y, Nano X

    Ni

    Cr

    Al

    Cu

    Co

    Ni

    +Ti

    Si

    Mo

    B

    P

    Mn

    Fe

    C

    Zr

    Ce+ La

    Balance

    15-

    45

    0.00

    1-18

    0.00

    1-15

    0.0

    01-

    10

    0.0

    01-

    10

    0.0

    1-

    12

    0.0

    01-

    10

    0.0

    01-

    6

    0.0

    01-

    8

    0.0

    01-

    5

    0.0

    1-

    15

    ≤ 0.3

    0.0

    7-3

    0.01

    1-1

    For further increase the abrasion or wear resistance, NanoYW=NanoY+15% (WC/10Co/4Cr), NanoXW=NanoX+15%(WC/10Co/4Cr)

    Thermal Spraying Process Suggestions:

    A1 Choose suitable parameters by trial specimens before the salt fog test formal specimen. The microstructure of the trial specimens has to have the uniform lamina without big round particles and oxidizing. The hardness of the trial specimens has to be not too high.

    A2 Use pressure air 50mm top from the coating for quick cooling out of the nozzles front and back of the spraying gun during spraying as above picture.

    A3 Choose Short Barrel. Long Spraying Distance. Low Flame Temperature. Keep the base metal temperature under 100℃. Spraying Gun angle 60-70° for NanoX and 90° for NanoY. Each pass thickness under 8um. When act as bond coat, the follow-up coating need quick cooling. Grinding or polishing the specimen to be metallic shiny before corrosion or abrasion test.

    3.Amorphous Nickel Spraying Powder of Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating Applications

    AMTmetalTech HVOF or HVAF Thermal Spraying Screw Rotors Powder  AMTmetalTech HVOF or HVAF Thermal Spraying Hydro Cylinders Powder  AMTmetalTech HVOF or HVAF Thermal Spraying Valve Balls Powder

    HVOF Spraying Screw Rotors               Thermal Spraying Cylinders                  HVAF Spraying Valve Balls   

    AMTmetalTech HVOF or HVAF Thermal Spraying Drive Pipes Powder AMTmetalTech HVOF or HVAF Thermal Spraying Pulp Rolls Powder  AMTmetalTech HVOF or HVAF Thermal Spraying Pistons Powder

    Thermal Spraying Drive Pipes               Thermal Spraying Pulp Rolls                   Thermal Spraying Pistons    

    AMTmetalTech Patent powder NanoX is suitable for the Severe Erosion, High Cavitation, High Abrasion or Wear, High Temperature Resist Sucker Rods, Screw Rotors, Cylinders, Valves, Drive Pipes, Pulp Rolls, Pistons, Hydro Turbine Blades, Seawater Erosion and replace chrome plating much longer life than Hastelloy / Inconel / Stellite etc.

    4. Amorphous Nickel Spraying Powder of Better Corrosion than Hastelloy, HV700-900, 1000℃ Abrasion, 50um Airtight Replace Chrome Plating Packaging

    The standard packaging is by vacuum bag per 5 or 10 kg. We can do according to the customer requirements for packaging. 

    5. AMTmetalTech Nano Spraying Powder Size Suggestion for Guns

    AMTmetalTech Nano Spraying Powder Size Suggestion for Guns

    Spraying Type

    Powder Feeding

    Nano Powder Size

    Suitable Spraying Guns

    Nano Powder Competitors

    ID-Coating

    ID≤80mm

    2-10um

    NanoHVOF,
    ID-NOVA/HVOF

    No Other Superfine Metal Powder

    ID≥80mm

    8-25um

    AK-ID HVAF, NanoHVOF, ID-NOVA/HVOF etc.

    No Other Fine Amorphous Powder

    OD-HVAF, Top Layer or Bond Coat

    All

    8-25um

    Kermetico, UniqueCoat etc.

    OD-HVOF, Top Layer or Bond Coat

    Axial/Center Feeding

    8-25um

    DJ2700, GTV-K2, JetKote etc.

    Radial/Vertical Feeding

    15-45um

    JP5000/8000, CastoJet, SUPERCote etc.

    Liquidmetal, Nanosteel, No other Nickel Amorphous Spraying Powder in the world

    OD-Detonation Spraying, Top Layer or Bond Coat

    All

    45-75um

    D-Gun etc.


     

    Please send us email about Nickel Amorphous HVAF or HVOF Tube Inside ID Spraying Fine Atomized Powder Better Corrosion risist than Hastelloy C276 / Inconel 625 / Stellite of severe Erosion, Cavitation, high temperature Abrasion resist Replacing Nickel Clad Tube; Ferro Powder for high speed Laser / PTA cladding / Plasma overlaying Replacing Chrome Plating for Cylinders / Pistons / Screw Rotors / Valve Balls / Stirrer Blade / Hydro Turbine; Tungsten Carbide Hardmetal Cemented Clad Mud Pump Liner / Tube / Sleeve / Glass Mold and Super Wear Plates for Brick Mould; PDC Diffusion Bonding, Diamond Bearing and Brazing etc. 